Effect of SO 2 on oxidation of metallic materials in CO 2 /H 2 O-rich gases relevant to oxyfuel environments: Effect of SO 2 on oxidation of metallic materials

In an oxyfuel plant, heat exchanging metallic components will be exposed to a flue gas that contains substantially higher contents of CO2, water vapor, and SO2 than conventionalflue gases. In the present study, the oxidation behavior of the martensitic steel P92 was studied in CO2-and/or H2O-rich gas mixtures with and without addition of SO2. For this purpose, the corrosion of P92 at 550 8C up to 1000 h in Ar–H2O–SO2, Ar–CO2–SO2, Ar–CO2–O2–SO2 and simulated oxyfuel gas (Ar–CO2–H2O–O2–SO2) was compared with the behavior in selected SO2-free gases. The oxidation kinetics were estimated by a number of methods such as optical microscopy, scanning electron microscopy with energy and wave length dispersive X-ray analysis, glow discharge optical emission spectroscopy, X-ray diffraction as well as transmission electron microscopy. The experimental results revealed that the effect of SO2 addition on the materials behavior substantially differed, depending on the prevailing base gas atmosphere. The various types of corrosion attack affected by SO2 could not be explained by solely comparing equilibrium activities of the gas atmospheres with thermodynamic stabilities of possible corrosion products. The results were found to be strongly affected by relative rates of reactions of the various gas species occurring within the frequently porous corrosion scales as well as at the scale/gas-and scale/alloy interfaces.Whereas SO2 addition to Ar–CO2 resulted in formation of an external mixed oxide/sulflde layer, the presence of SO2 in oxyfuel gas and in Ar–H2O–SO2 resulted in Fe-sulflde formation near the interface between inner and outer oxide layer as well as Cr-sulflde formation in the alloy. In the latter gases, the presence of SO2 seemed to have no dramatic effect on oxide scale growth rates.