Mechanical properties of ZrB2- and HfB2-based ultra-high temperature ceramics fabricated by spark plasma sintering

Flexural strengths at room temperature, at 1400°C in air and at room temperature after 1h oxidation at 1400°C were determined for ZrB2- and HfB2-based ultra-high temperature ceramics (UHTCs). Defects caused by electrical discharge machining (EDM) lowered measured strengths significantly and were use...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:Journal of the European Ceramic Society 2013-07, Vol.33 (7), p.1373-1386
Hauptverfasser: Zapata-Solvas, E., Jayaseelan, D.D., Lin, H.T., Brown, P., Lee, W.E.
Format: Artikel
Sprache:eng
Schlagworte:
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:Flexural strengths at room temperature, at 1400°C in air and at room temperature after 1h oxidation at 1400°C were determined for ZrB2- and HfB2-based ultra-high temperature ceramics (UHTCs). Defects caused by electrical discharge machining (EDM) lowered measured strengths significantly and were used to calculate fracture toughness via a fracture mechanics approach. ZrB2 with 20vol.% SiC had room temperature strength of 700±90MPa, fracture toughness of 6.4±0.6MPa, Vickers hardness at 9.8N load of 21.1±0.6GPa, 1400°C strength of 400±30MPa and room temperature strength after 1h oxidation at 1400°C of 678±15MPa with an oxide layer thickness of 45±5μm. HfB2 with 20vol.% SiC showed room temperature strength of 620±50MPa, fracture toughness of 5.0±0.4MPa, Vickers hardness at 9.8N load of 27.0±0.6GPa, 1400°C strength of 590±150MPa and room temperature strength after 1h oxidation at 1400°C of 660±25MPa with an oxide layer thickness of 12±1μm. 2wt.% La2O3 addition to UHTCs slightly reduced mechanical performance while increasing tolerance to property degradation after oxidation and effectively aided internal stress relaxation during spark plasma sintering (SPS) cooling, as quantified by X-ray diffraction (XRD). Slow crack growth was suggested as the failure mechanism at high temperatures as a consequence of sharp cracks formation during oxidation.