Strongly segregated cubic microdomain morphology consistent with the double gyroid phase in high molecular weight diblock copolymers of polystyrene and poly(dimethylsiloxane)

We report the observation of a cubic phase consistent with the double gyroid structure in strongly segregated diblock copolymers of PS-b-PDMS over a volume fraction (φPDMS) range of ~0.39 to 0.45. The samples have respective molecular weights of 127 kg/mol and 73 kg/mol and degree of segregation Nχ equal to 187 and 106, respectively, at annealing temperature of 130 °C. It is important to highlight that two out of the total four samples investigated, exhibited hexagonally close packed cylindrical domains of PDMS and alternating lamellae at φPDMS = 0.39 and 0.45, respectively, indicating the possible narrow range of the DG morphology for the specific diblock copolymers.