폴리카보네이트 임시수복재료의 물성 평가

Purpose: The purpose is to test and evaluate the physical properties of commonly used temporary restoration materials and newly emerged materials. Materials and Methods: Four groups of polymer materials were evaluated: Polymethyl methacrylate (PMMA) 2 groups, Polyetheretherketone (PEEK), Polycarbonate. Four physical properties were tested: surface hardness, bending strength, abrasion resistance during wear, wear behavior. The 3-axis bending strength and Vickers hardness test were measured using a universal testing machines respectively. The microstructure was observed with a scanning electron microscope and weight comparison was evaluated after 100,000 chewing tests using a chewing simulator. Kruskal wallis test was performed to evaluate statistical significance. Results: The four groups showed the highest flexural strength and Vickers hardness of PEEK, followed by PC, PMMA-H, PMMA-T. Microstructure observation also showed the least surface roughness in the PEEK group, followed by PC, PMMA-H, PMMA-T. Conclusion: PC is considered to have sufficient mechanical properties that can be applied to the manufacture of temporary teeth. However, further studies, such as biocompatibility, are considered to be necessary for practical clinical applications. 목적: 현재 상용화하여 사용되는 임시 수복물 재료와 새롭게 대두되는 재료들의 기계적 성질을 실험하고, 평가하는 것이다. 연구 재료 및 방법: Polymethyl methacrylate (PMMA) 2종, polyetheretherketone (PEEK), polycarbonate 4군의 고분자 재료들을 평가하였고, 표면 경도, 굴곡강도, 저작 시 마모도, 마모 양상 4가지의 기계적 물성을 실험하였다. 시편의 3축 굽힘 강도와 비커스 경도 테스트는 각각 만능 시험기를 사용하여 측정하였고, 저작 시험기를 이용하여 100,000회의 저작 시험 후 주사 전자 현미경으로 미세구조를 관찰하고 전, 후 무게를 비교하였다. 통계적 유의성 평가를 위해 kruskal wallis test를 시행하였다. 결과: PEEK의 굽힘 강도와 비커스 경도가 가장 높게 나타났으며, PC, PMMA-H, PMMA-T 순으로 나타났다. 미세구조 표면은 PEEK 군에서 거칠기 형태가 가장 적게 나타났으며, PC, PMMA-H, PMMA-T 순으로 적게 나타났다. 결론: PC는 임시치아 제작에 적용할 수 있는 충분한 기계적 성질을 가진 것으로 사료된다. 그러나, 실제 임상 적용을 위해서는 생체 친화성과 같은 추가적인 연구가 필요할 것으로 사료된다.