Effect of gas environment on properties of particles prepared by spray pyrolysis of metal nitrates

Particles in different states of oxidation were prepared by spray pyrolyses of aqueous solutions of silver and copper nitrates under different gas environments: air, nitrogen or mixture gas of 10 vol%H 2 -N 2 , respectively. Silver nitrate was converted to phase-pure silver at temperatures below 500 °C whose densification and crystallization were completed around 500 °C, irrespective of the gas environment. On the other hand, phase-pure copper(II) oxide was formed from copper nitrate up to 1,000 °C with air, but below 800 °C with nitrogen, above which copper(I) oxide was produced. Phase-pure copper particles were obtained with the mixture gas at temperatures above 400 °C. Copper(I) oxide was sintered and crystallized more easily than copper(II) oxide. The rates of the metallization, sintering and crystallization of copper were between those of silver and nickel.