리포솜이 함유된 N-이소프로필아크릴아마이드의 공중합체로부터 온도에 따른 약물의 방출

Thermosensitive poly(N-isopropylacrylamide) gels containing temperature-sensitive liposomes showing temperature-dependent sol-gel transition were prepared. The surface of temperature-sensitive liposome was modified with copolymers of N-isopropylacrylamide and octadecylacrylate, which exhibited a lower critical solution temperature at around 30 $^{\circ}C$ After mixing the modified temperature-sensitive liposomes with poly(N-isopropylacrylamide) solution, the temperature-sensitive 1iposomes formed physically cross-linked gels through heating the solution above their lower critical solution temperatures. The release of drug from temperature-sensitive liposomes was determined by measuring fluorescence intensity. The drug release from temperature-sensitive liposomes in poly(N-isopropylacrylamide) gel gradually showed sustained-release with increasing temperature. 온도에 의존하여 졸-젤 전이를 나타내는 온도민감성 리포솜을 함유하는 폴리 N-이소프로필아크릴아마이드 젤을 제조하였다. 온도민감성 리포솜의 표면은 3$0^{\circ}C$에서 하한임계용액온도를 나타내는 N-이소프로필아크릴아마이드와 옥타데실아크릴레이트의 공중합체를 이용하여 변형시켰다. 표면이 변형된 온도민감성 리포솜을 폴리 N-이소프로필아크릴아마이드 수용액에 혼합하였다. 혼합용액을 하한임계용액온도 이상으로 가열했을 때 물리적으로 가교결합이 이루어진 젤의 형태가 이루어지며, 이때 온도 민감성 리포솜이 함유된 폴리 N-이소프로필아크릴아마이드 젤이 만들어진다. 온도민감성 리포솜으로부터 약물의 방출은 형광강도를 측정하여 결정하였다. 폴리 N-이소프로필아크릴아마이드 젤 내부의 온도민감성 리포솜으로부터 약물의 방출은 온도가 증가할수록 지속적인 방출을 나타내었다.