유화-확산법에 의해 얻어진 폴리(비닐 아세테이트) 나노 방향 입자의 특성 및 방출 거동

In this study, nano-sized poly(vinyl acetate) (PVAc) particles containing lavender oil as a core material were prepared by using emulsification-diffusion method. Effects of experimental parameters on the characteristics and the release behavior were examined with a field emission- scanning electron microscope, an electrophoretic light scattering spectrophotometer, a visible spectrophotometer and a high performance liquid chromatography The resulting aromatic particles could be prepared in nano-sized globular shapes with the mean particle size of 224 nm by controlling the experimental conditions. From the evaluation of release properties of aromatic PVAc nanoparticles with or without PVA coating, it was found that the aromatic particles coated with PVA show more sustaining and stable release behaviors. Our research on aromatic PVAc nanoparticles could be applied for durable fragrant finishing for textiles, leather products and so on. 본 연구에서는 라벤더 오일을 심물질로 이용하여 나노크기의 폴리(비닐 아세테이트)(poly(vinyl acetate), PVAc) 방향 입자를 유화-확산법으로 제조하였다. 방향 물질의 방출 시기와 속도 조절로 방향 캡슐의 지속성과 내구성을 얻기 위하여 제조 조건에 따른 나노 방향 입자의 특성과 방출 거동을 주사 전자 현미경, 전기 영동 광산란 분광 분석기, 자외선-가시광선 분광 분석기 및 고성능 액체 크로마토그래피를 이용하여 고찰하였다. 제조된 방향 입자는 실험 조건을 조절함에 따라 평균 입자 크기가 224 nm인 구상 나노 입자로 제조하는 것이 가능하였으며, 170시간 동안의 방출 거동을 비교.평가한 결과 PVA로 코팅한 방향 입자가 더 지속적이고 안정적인 초기 방출 거동을 보임을 확인할 수 있었다. 본 연구의 PVAc 나노 방향 입자는 직물 및 피혁제품 등에 대한 내구성 방향가공에 적용될 수 있을 것으로 기대된다.