Effect of post-deposition annealing on the structural, optical and electrical properties of IGZO films
IGZO thin films were deposited on glass substrates via RF magnetron co-sputtering with In 2 O 3 and GZO targets. The films were then vacuum annealed at 100°C, 200°C and 300°C for 30 minutes to investigate the effects of the annealing temperature on the structural, electrical, and optical properties...
Gespeichert in:
Veröffentlicht in: | Electronic materials letters 2015, 11(3), , pp.481-484 |
---|---|
Hauptverfasser: | , , , , |
Format: | Artikel |
Sprache: | eng |
Schlagworte: | |
Online-Zugang: | Volltext |
Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
Zusammenfassung: | IGZO thin films were deposited on glass substrates via RF magnetron co-sputtering with In
2
O
3
and GZO targets. The films were then vacuum annealed at 100°C, 200°C and 300°C for 30 minutes to investigate the effects of the annealing temperature on the structural, electrical, and optical properties of the films. Although XRD patterns demonstrated that all films had an amorphous phase regardless of annealing temperature, electrical resistivity decreased to as low as 3.2 × 10
-4
Ω cm at an annealing temperature of 300°C. The optical transmittance in the visible wavelength region also improved from 80 to 83%. The figure of merit shows that IGZO films annealed at 300°C have the higher optical and electrical performance than other films prepared under different conditions in this study. |
---|---|
ISSN: | 1738-8090 2093-6788 |
DOI: | 10.1007/s13391-014-4410-1 |