High-Temperature Corrosion of T92 Steel in N2/H2O/H2S-Mixed Gas
The ASTM T92 steel was corroded at 600 oC and 800 oC at 1 atm of N2/3.1%H2O/2.42%H2S-mixed gas. The formed scales were thick and fragile. They consisted primarily of the outer FeS scale and the inner(FeS, FeCr2S4)-mixed scale containing a small amount of the Cr2O3 scale. This indicated that corrosio...
Gespeichert in:
| Veröffentlicht in: | Corrosion science and technology 2016, 15(3), , pp.125-128 |
|---|---|
| Hauptverfasser: | , , , , , |
| Format: | Artikel |
| Sprache: | eng |
| Schlagworte: | |
| Online-Zugang: | Volltext |
| Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
| Zusammenfassung: | The ASTM T92 steel was corroded at 600 oC and 800 oC at 1 atm of N2/3.1%H2O/2.42%H2S-mixed gas.
The formed scales were thick and fragile. They consisted primarily of the outer FeS scale and the inner(FeS, FeCr2S4)-mixed scale containing a small amount of the Cr2O3 scale. This indicated that corrosionoccurred mainly via sulfidation rather than oxidation due to the H2S gas. Since FeS was present throughoutthe whole scale, T92 steel was non-protective, displaying high corrosion rates. KCI Citation Count: 0 |
|---|---|
| ISSN: | 1598-6462 2288-6524 |
| DOI: | 10.14773/cst.2016.15.3.125 |