개선된 단일상 합성법을 이용한 티올화 나노 금의 합성 및 확인

One-phase method to prevent the initial formation of Ag(I) thiolate layered materal from the mixture of $AgNO_3$ and thiols was previously developed to generate TP (Thiolate-Protected)-nanosilver. In this modified method, $AgNO_3$ is added to the mixtures of $NaBH_4$ and thiols in ethanol. This method was so successful that it was applied to synthesize TP-nanogold and nanoplatinum. The synthesis and characterization of these nanoparticles by ultraviolet-visible (UV-vis) absorption spectra, transmission electron microscopy (TEM) pictures, X-ray powder differaction (XRD) patterns and infrared(IR) spectra are described. The results show that colloidal nanoparticles are spherical or oval shape and the mean sizes for TP-nanogold and nanoplatinum are about 3~7 nm and below 2 nm, respectively. The conformation of polymethylene [$-(CH_2)_7-$] sequence in octanethiolate attached to nanogold was elucidated as trans. 앞선 연구에서 TP(Thiolate-Protected)-나노은의 합성 시 초기에 형성되는 티올화 은 층간화합물의 형성을 막기 위하여 에탄올에 녹아있는 $NaBH_4$와 티올에 $AgNO_3$를 첨가하는 개선된 단일상 합성법을 보고하였다. 본 연구에서는 이 합성법을 보다 일반화하기 위하여 TP-나노금과 나노백금의 합성에 적용하였다. 합성된 생성물의 나노크기, 형상 및 금속에 부착된 티올의 배열은 UV-vis. 스펙트럼, 투과 전자 현미경 사진, X-선 회절 패턴 및 적외선 분광 스펙트럼을 이용하여 규명 하였다. TP-나노금과 나노백금은 구형 및 타원형의 형태를 하고 있으며 입자크기는 각각 약 3~7 nm와 약 2 nm 이하로 나타나고 있다. 한편 TP-나노금의 표면을 감싸는 옥탄티올 음이온의 메틸렌 사슬 [$-(CH_2)_7-$]의 메틸렌 배향은 trans임을 보여주고 있다.