Improvement of luster consistency between the p-Pad and the n-Pad of GaN-based light-emitting diodes via the under-etching process

For improvement of the light extraction efficiency of GaN-based lateral light-emitting diodes (LEDs), a p-GaN surface was textured through a low-temperature (850 °C) p-GaN growth process. However, the p-GaN texturing process caused luster inconsistency between the n-pad and the p-pad due to the roughness difference between the indium-tin oxide (ITO) and the n-GaN beneath the pads, which decreased the image recognition rate and accuracy during the wire bonding process for LED packaging. Therefore, an under-etching process was proposed to improve the luster consistency between the p-pad and the n-pad of GaN-based LEDs with a naturally textured p-GaN surface. The under-etching process decreased the roughness of the exposed n-GaN surface from 109 nm to 73.1 nm, which was similar to the roughness (74.8 nm) of the ITO surface. Optical microscopy showed that LEDs with a naturally textured p-GaN surface exhibited excellent luster consistency between the n-pad and the p-pad after the proposed under-etching process had been applied. Further analysis indicated that the LEDs with a naturally textured p-GaN surface showed no degradation of optical or the electrical performance after the proposed under-etching process had been applied. At a 20-mA injection current, the light output power of a LED with naturally a textured p-GaN surface was 8.7% higher than that of a LED with a smooth p-GaN surface.