하수슬러지 소각 비산재를 이용한 입상비료 조립 및 특성분석

This study assessed feasibility of making granular fertilizer with fly ash from a sewage sludge incinerator in Korea. Composition, characteristics, strength, and heavy metal contents of the granular fertilizers were investigated. Due to its high contents of phosphorus, fly ash from a sewage sludge incinerator could be used to make fertilizers. Granulation rates (2-4 mm granules) over 80% could be achieved as the fly ash contents were 15% or less of the fertilizer. Leaching tests of the fertilizers, based upon the Korean Standard Methods for Solid Wastes, showed the concentrations of heavy metals less than the risk limits. However, contents analysis of the fertilizers, based upon the Korean Standard Methods for Soils, experienced higher levels of heavy metals than the risk limits as the fly ash content exceeded 7% of the fertilizer. Thus, the fly ash needs to be added less than 7% of the fertilizer if there is no pretreatment to remove heavy metals. 생활하수슬러지만 소각하는 시설에서 발생되는 비산재를 비료 제조시 주원료 또는 부원료로 활용하기 위해 비산재를 원료로 비료를 제조하고 구성성분을 분석하였다. 비산재를 포함해 제작된 비료의 구성 및 물성, 강도, 중금속에 대한 위해성 등을 분석하였다. 비산재는 충분한 인을 함유하여 비료의 원료로 사용될 수 있으나, 비산재를 주원료(40% 이상 포함)로 비료를 제작할 경우 조립화율(2-4 mm 입자 형성율)을 80% 이상 달성할 수 없었다. 비산재를 보조원료로 첨가하여 비료를 제조할 경우, 비산재 함유량을 15%이하로 유지하면 조립화율을 80% 이상 달성할 수 있었다. 비산재를 보조원료로 조립화된 비료의 중금속 분석결과, 폐기물공정시험기준인 용출실험에서는 위해성이 없는 것으로 나타났다. 그러나 토양오염공정시험의 함량분석 상으로는 비산재 함유량이 높아짐에 따라 카드뮴 등 중금속 위해성을 초과하는 항목이 발생되었다. 따라서 비료제작시 비산재를 보조원료로 투입할 경우 중금속을 제거하기 위한 전처리를 하지 않는다면 비료원료의 비산재 함유량을 7% 이하로 유지하는 것이 바람직하다.