알루미늄 열용사 코팅된 AA5083-H321의 내식성 평가

In this study, anti-corrosion effect was investigated through various electrochemical experiments after applying Al thermal spraying technology to AA5083-H321. Open circuit potential and anodic polarization curves were analyzed through electrochemical experiments in natural seawater. The shape of the surface was observed using a scanning electron microscope (SEM) and a 3D microscope before and after the experiment. Component and crystal structure were analyzed through EDS and XRD. As a result, the surface roughness of AA5083-H321 and the Al thermal sprayed coating layer increased due to surface damage caused by anodic dissolution reaction during the anodic polarization experiment. The corrosion rate of AA5083-H321 was relatively low because the Al thermal spray coating layer contained structural defects such as pores and crevices. Nevertheless, the open circuit potential of the Al thermal spray coating layer in natural seawater was measured about 0.2 V lower than that of AA5083-H321. Thus, a sacrificial anode protection effect can be expected.