Fabrications and dielectric performances of novel composites: Calcium copper titanate / Polyvinylidene fluoride

CCTO (Calcium copper titanate) powder as inorganic filler was synthesized by the Sol-gel method firstly. CCTO/PVDF (Polyvinylidene fluoride) composite was fabricated by solution mixing based on high temperature resistance of PVDF and insulated property of CCTO. The composite of CCTO/PVDF were characterized by X-ray diffraction, Fourier Transform infrared spectroscopy, Scanning Electron Microscope and impedance analysis. The results showed that the addition of CCTO and increasing in its content did not affect the phase- and micro-structure of the composites,but the increase of CCTO content can induce the generation of C–F new bonds. PVDF/CCTO composites were enhanced in performance of thermal and frequency-depended stability with increasing in the fraction of CCTO. The dielectric constant of CCTO/PVDF composite materials with 50% CCTO achieved to a maximum value of 50 almost, which is 5 times higher the pure PVDF. The conductivity felled into 10−8 to 10−1 S m−1 during the frequency of 102–108 Hz. The composite material would be expected to be applied in the field of integrated circuit. The dielectric (a) & (e), loss (b) & (f), intensity (c) and conductivity (d) performances of CCTO/PVDF composite. [Display omitted] •Calcium copper titanate powder was synthesized by the Sol-gel method firstly.•CCTO/PVDF composite was fabricated by solution mixing at the first time.•Dielectric constants of CCTO 50%/PVDF composite gets its maximum value of 50, 5 times higher than pure PVDF.