Estimation of Delamination Crack Depth Using Passive Thermography

Passive thermography is used to monitor small increases in temperature resulting from delamination damage formation in a composite hat-stiffened panel during quasi-static loading. The heating is composed of two heat generation components. The first component is an instantaneous response due to a strain release during quasi-static loading. The second component is mechanical heating, at the interface of failure, due to fracture damage. This second component produces a transient rise in temperature that is a function of the damage depth and thermal diffusivity. The first component defines the thermal start time for the transient response. A one-dimensional thermal model is used to determine the damage depth. The results are compared to ultrasonic and X-ray CT data. The advantages and limitations of the thermal technique for damage depth detection are discussed.