전자 개폐기용 바이메탈 소재(Fe-Ni / Fe-Ni-Mo)의 부식거동

This study examined the corrosion behavior of bimetal materials composed of Fe-Ni alloy and Fe-Ni-Mo alloy, both suitable for use in electromagnetic switches. Electrochemical polarization and weight loss measurements revealed that, in contrast to Fe-Ni alloy, which exhibited pseudo-passivity behavior, Fe-Ni-Mo alloy had higher anodic current density, displaying only active dissolution and greater weight loss. This indicated a lower corrosion resistance in the Fe-Ni-Mo alloy. Equilibrium calculations for the phase fraction of precipitates suggested that the addition of 1 wt% Mo may lead to the formation of second-phase precipitates, such as Laves and M6C, in the γ matrix. These precipitates might degrade the homogeneity of the passive film formed on the surface, leading to localized attacks during the corrosion process. Therefore, considering the differences in corrosion kinetics between these bimetal materials, the early degradation caused by galvanic corrosion should be prevented by designing a new alloy, optimizing heat treatment, or implementing periodic in-service maintenance.