Horseradish peroxidase가 변성된 탄소복합 바이오센서 개발 및 전기화학적 H 2 O 2 분석

A sol-gel derived carbon composite electrodes (CCEs) were fabricated by mixing horseradish peroxidase (HRP), sol of tetraethoxysilane (TESO), and graphite powder. The HRP solution was added to the sol solution of TEOS, and then graphite powder was added to this mixture. The resulting carbon ceramic network effectively encapsulated HRP and shows a catalytic reduction starting at -0.2 V for $H_2O_2$. The optimum conditions for $H_2O_2$determination have been characterized with respect to the enzyme loading ratio and pH. The linear range and detection limit of $H_2O_2$ detection were from 0.2 mM to 2.2 mM and 0.035 mM, respectively. The common electroactive interferences such as ascorbic acid, acetaminophene, and uric acid were not affected upon the response to $H_2O_2$ at the HRP biosensor due to low detection potential. Horseradish peroxidase (HRP), alkoxysilane인 TEOS의 겔 용액과 graphite를 혼합하여, 전기전도성을 나타내고 재사용이 가능하며 안정성을 향상시킨 carbon composite electrodes (CCEs) 바이오센서를 제작하였다. TEOS의 졸-겔 전이반응을 이용하여 HRP를 silicate gel network포획시킨 바이오센서는 -0.2 V에서 $H_2O_2$의 환원이 시작되었으며, HRP의 함량과 pH를 변화시켜 최적 분석 조건을 구하였다. 분석 최적 조건에서 검량선 및 검출한계를 구한 결과, 0.2~2.2 mM의 $H_2O_2$ 농도 범위에서 직선적인 감응을 나타내며 검출한계는 0.035 mM이었다. ascorbic acid, acetaminophene, uric acid의 방해작용을 조사한 결과 $H_2O_2$의 전기화학적 분석에 영향을 주지 않았다.