접착시스템의 소수성이 Low-shrinkage silorane resin과 상아질의 미세인장강도에 미치는 영향

Objectives: The purpose of this study was to evaluate ${\mu}TBS$ (microtensile bond strength) of current dentin bonding adhesives which have different hydrophobicity with low-shrinkage silorane resin. Materials and Methods: Thirty-six human third molars were used. Middle dentin was exposed. The teeth were randomly assigned to nine experimental groups: Silorane self-etch adhesives (SS), SS + phosphoric acid etching (SS + pa), Adper easy bond (AE), AE + Silorane system bonding (AE + SSb), Clearfil SE bond (CSE), CSE + SSb, All-Bond 2 (AB2), AB2 + SSb, All-Bond 3 (AB3). After adhesive's were applied, the clinical crowns were restored with Filtek LS (3M ESPE). The 0.8 mm ${\times}$ 0.8 mm sticks were submitted to a tensile load using a Micro Tensile Tester (Bisco Inc.). Water sorption was measured to estimate hydrophobicity adhesives. Results: ${\mu}TBS$ of silorane resin to 5 adhesives: SS, 23.2 MPa; CSE, 19.4 MPa; AB3, 30.3 MPa; AB2 and AE, no bond. Additional layering of SSb: CSE + SSb, 26.2 MPa; AB2 + SSb, 33.9 MPa; AE + SSb, no bond. High value of ${\mu}TBS$ was related to cohesive failure. SS showed the lowest water sorption. AE showed the highest solubility. Conclusions: The hydrophobicity of adhesive increased, and silorane resin bond-strength was also increased. Additional hydrophobic adhesive layer did not increase the bond-strength to silorane resin except AB2 + SSb. All-Bond 3 showed similar ${\mu}TBS$ & water sorption with SS. By these facts, we could reach a conclusion that All-Bond 3 is a competitive adhesive which can replace the Silorane adhesive system. 연구목적: 본 연구의 목적은 다양한 소수성을 지닌 최신 상아질 접착시스템과 저수축 silorane 레진의 미세인장결합강도를 평가하는 것이다. 연구 재료 및 방법: 36개의 갓 발치된 제3대구치를 이용했다. Low-speed diamond saw를 사용하여 교합면에 평행하게 치관을 잘라 middle dentin을 노출시켰다. 치아를 무작위로 9 group으로 나눴다. Silorane self-etch adhesives (SS), SS + phosphoric acid etching (SS + pa), Adper Easy bond (AE), AE + Silorane system bonding (AE + SSb), Clearfil SE bond (CSE), CSE + SSb, All-Bond 2 (AB2), AB2 + SSb, All-Bond 3 (AB3). 접착제를 적용한 후에 Filtek LS (3M ESPE)를 2 mm씩 3회 적층충전하였다. 각 층은 40s씩 광중합하였다. 0.8 mm ${\times}$ 0.8 mm stick을 Micro Tensile Tester로 1 mm/min cross-head speed의 인장력을 가하였다. 파절양상를 관찰하기 위해 광학현미경을 이용하였다. 5가지 접착제의 소수성정도를 결정하기위해 water sorption test하였다. 결과: silorane 레진과 5가지 접착제의 ${\mu}TBS$: SS, 23.2 ${\pm}$ 6.9 MPa; CSE, 19.4 ${\pm}$ 4.4 MPa; AB3, 30.3 ${\pm}$ 4.0 MPa; AB2와 AE, no bond. Additional layering of SSb: CSE + SSb, 26.2 ${\pm}$ 10.3 MPa; AB2 + SSb, 33.9 ${\pm}$ 7.3 MPa; AE + SSb, no