레진시멘트의 색안정성에 대한 가속시험

The purpose of this study was to evaluate the color stability of resin cements with accelerated test. Four dual curing resin cements: Panavia-F (KURARAY). Duolink (BISCO), Variolink-II (Ivoclar Vivadent), and RelyX Unicem (3M ESPE) and 1 self curing resin cement: Resiment CE (j. l. Blosser) were used in this study. In control group, Gradia Anterior (GC) composite resin and Tescera Dentin (Bisco) indirect composite were used. Ten disk shape specimens were made from each resin cement. The specimens were subjected to an accelerated aging process in a refrigerated bath circulator at 60$^{\circ}C$ for 15 and 30 days. Spectrophotometric analyses were made before and after 15 days and 30 days of accelerated aging time. The color characteristics ($L^*,\;a^*,\;b^*$) and the color difference (${\Delta}E^*$) of the specimens before and after immersion were measured and computed. Regardless of type of the resin cements, $L^*$ value was decreased and $a^*$ value was increased, but there were no significant difference. But $b^*$ value was increased significantly (p < 0.05). Tescera inlay showed least color change (p < 0.05), but Gradia showed notable color change after 15 days. After 30 days on accelerated aging, ${\Delta}E^*$ value was increased (Panavia-F < Variolink-II < Resiment CE < Duolink < Unicem) (p < 0.05). but there were no significant difference among Panavia-F, Variolink-II, and Resiment CE groups. After 30 days of accelerated aging, ${\Delta}E^*$ value of all resin cements were greater than 3.0 and could be perceived by the human eye. 본 연구는 레진 시멘트의 색 안정성을 평가하여, 레진 시멘트의 변색에 의한 심미 수복물의 실패의 가능성을 평가하고자 시행하였다. 4종의 이원중합형 레진 시멘트인 Panavia-F (PA, KURARAY), Duolink (DL; BISCO), Variolink II (VL; Ivoclar Vivadent), 및 RelyX Unicem (UC: 3M ESPE)과 1종의 자가중합형 레진 시멘트인 Resiment Ready-Mix (with fluoride) CE (RM: j.1.Blosser)를 사용하였으며, 대조군으로 복합레진 Gradia Direct (CD ; GC)과 복합 레진 인레이용 Tecera Dentin A3 (TE ; Bisco)를 사용했다. 각 재료 당 직경 6.5 mm, 두께 4.5 mm의 디스크형 시편 10개를 제작하였다. 중합 후 시편은 분광색채계측기인 Spectrolino (GretagMacbeth)를 이용해 CIE $L^*a^*b^*$값을 측정하고 가속시험을 위해 빛이 차단된 refrigerated bath circulator에서 60$^{\circ}C$ 증류수에 30일간 보관 후에 색 측정을 시행하고, 시험 전 후의 색차를 계산하였다. 가속 시험 후 $L^*$ 값은 감소하는 양상을 보였고, $a^*$ 값은 증가하는 양상을 보였지만 유의한 차이는 없었다. 반면 $b^*$ 값은 유의하게 증가하였다 (p < 0.05). TE가 15일과 30일 모두에서 가장 적은 색변화 (p < 0.05)를 보인 반면 GD는 15일 가속 실험 후 큰 색변화를 보였다. 30일 가속 실험 후 PA, VL, RM, DL 그리고 UC 순으로 ${\Delta}E^*$값이 커졌으며 (p < 0.05), 30일 후 모든 레진시멘트 들은 육안으로 변색을 인지 할 수 있는 3 이상의 ${\Delta}E^*$ 값을 보였다.