실리카광물의 산침출 정제방법에 따른 불순물 변화 연구

Purification of silica mineral was compared with various leaching methods such as shaking, stirring, ultrasonic with 2.5% HF/HCl solution. Among them, ultrasonic method showed a best leaching effect. From the leaching experiment, Na, K, Fe, Al exist as the major impurity elements. The removal rate of Al, Fe showed little difference with various leaching methods but Ca, Mn, Na were very different. Four kinds of silica mineral (>99% purity) after physical purification treatment were used for ultrasonic leaching experiment. Among them IN-Si had a highest impurity removal rate. Ca, Cr, K, Zn were removed above 80% using ultrasonic leaching method and Fe was also removed above 60%. But Al showed 10~60% removal rate with different samples. 실리카 광물의 정제를 위해 다양한 침출방법을 사용하여 침출특성을 비교하였다. 2.5% HF/HCl 산 침출용액을 사용하여 진동, 젓기, 초음파를 이용한 침출실험에서 초음파에 의한 침출방법이 가장 좋은 불순물 제거 효율을 나타내었다. 실험결과 Al, Ca, Fe, K, Na 등이 주 불순물로 존재하고 있었으며, 그 외 미량의 불순물로 Ba, Cu, Sr, Ti 등이 존재하였다. 실리카 광물중의 불순물 함량은 침출법에 의해 대부분 감소되었다. 또한 주 불순물인 Al, Fe의 경우 침출방법에 따라 제거율이 크게 차이나지 않았으나, Ca, Mn, Na 등은 제거율이 현저히 다른 양상을 나타내었다. 물리적 정제과정을 거친 4종류의 실리카 광물(순도 99% 이상)을 초음파를 이용한 산 침출법으로 정제한 결과, 총 불순물의 양은 NK-Si와 GR-Si이 적었으나 산 침출과정을 거친 후에는 IN-Si 실리카의 불순물 량이 가장 적게 나타났다. 불순물 중 Ca, Cr, K, Zn 등은 거의 80% 이상 초음파 침출법에 의해 제거되었고, 주 불순물인 Al의 경우 시료에 따라 10~60%의 제거율 차이를 나타내며 Fe는 모든 시료에서 60% 이상 제거되었다.