Acetic acid and succinic acid bonded polyamine-polyurea(CPPI and SAPPI) resins were synthesized from the reaction of polyethylenimine-polymethylenepolyphenylene isocyanate(PPI) resin as matrix polymer and chloroacetic acid and chlorosuccinic acid respectively. These resins were confirmed with infrared spectrometry and elemental analysis. The adsorption characteristics of the chromium(III) and dichromate(or chromate) ions on the resins were studied by measuring distribution coefficients($K_d$) with changing pH of the solution. It was thought that these ions were adsorbed by ion exchange mechanism. Chromium(III) and dichromate ion could be separated with stepwise elution method by changing pH of the eluent using SAPPI resin packed column($0.6cm(i.\;d.){\times}10cm(L.)$). Also, dichromate ion could be preconecntrated with CPPI resin column by a concentration factor of 50. 아세트산과 숙신산이 결합된 폴리아민-폴리우레아(CPPI와 SAPPI) 수지는 폴리에틸렌이민-폴리메틸렌폴리페닐렌 이소시안에이트(PPI) 고분자와 클로로 아세트산 또는 클로로 숙신산의 반응으로 각각 합성되었다. 이 수지들은 적외선 분광광도법 및 원소분석법으로 구조를 확인하였다. 이 수지들에 대한 3가와 6가 크롬의 흡착특성은 용액의 pH를 변화시키면서 뱃치법에 의하여 분포계수($K_d$)를 측정하여 조사하였다. 3가와 6가 크롬은 이온교환반응으로 폴리아민-폴리우레아 수지에 흡착되는 것으로 생각되었다. 이들의 최적 분리조건을 발견하고, 단지 pH를 변화시키는 단계적 용리법에 의하여 이들의 SAPPI 수지관(내경 0.6cm, 길이 10cm)으로 분리하였다. 또한 6가 크롬은 CPPI 수지관에 의하여 50배의 농축인자로 농축할 수 있다.