Effect of specific surface area of MWCNTS on surface roughness and delamination in drilling Epoxy/Glass Fabric Composite

In this study the effect of specific surface area of the MWCNTs on the drilled hole qualities was investigated. Epoxy araldite LY556 with hardener HY951 and E-glass coarse plain weave fabric are used for the fabrication of reference material (specimen A). Multi-WalledCarbon Nanotubes (MWCNTs) with diameters 500 m2 g−1. MWCNTs in specimen C had a specific surface area >110 m2 g−1. Drilling experiments were conducted on all the three specimens. Two dimensional delamination factor and the surface roughness of the inner wall of the drilled holes were investigated using Grey Relational Analysis (GRA) and Analysis of variance (ANOVA). Two dimensional delamination factor showed better performance from specimen B and specimen C in comparison with specimen A suggesting improvement in the bonding between epoxy and the glass fiber in the presence of MWCNTs. Similar observations were made for surface roughness of the inner wall of the drilled holes at 1250 rpm. Whereas the presence of MWCNTs (Specimen B and specimen C) produced poor surface finish at 500 rpm in comparison with specimen A. Variations in the hole quality characteristics between specimen B and specimen C was marginal with better observations in specimen C.