Fabrication of Potentiometric Enzymatic Glucose Biosensor Based on Graphene and Magnetic Beads

In this paper, ruthenium dioxide (RuO 2 ) electrodes were fabricated by radio frequency sputtering and screen-printed technique, and RuO 2 sensing films could be as pH sensor to measure different pH solutions. The average sensitivity and linearity of pH sensor were 51.847 mV/pH and 0.987, respectively. A glucose biosensor could be prepared through casting glucose oxidase (GOx) on RuO 2 electrode, so the flexible arrayed glucose biosensors modified by magnetic beads (MBs) and graphene (GR) were developed in this paper. In preparation processes, GR solution was first cast on the RuO 2 , then we introduced carbodiimide hydrochloride (EDC) to connect glucose oxidase (GOx) and MB by covalent bond. Finally, MBs-GOx-nafion composite was dropped on RuO 2 to complete preparation of the RuO 2 /GR/MB-GOx-Nafion glucose biosensor. The electrochemical impedance spectra (EIS) was used to investigate the capability of electron transfer of the different electrodes, and it was found that the additions of MBs and GR which had excellent electric conductivity could decrease the electron transfer resistance (R ct ) from the experiment results. Besides, EIS could also be used to demonstrate whether the glucose biosensors had already been completely modified by MBs and GR through the different resistances of the biosensors. Furthermore, the glucose biosensor modified by MBs and GR had the superior performance, the average sensitivity and linearity of RuO 2 /GR/MB-GOx-Nafion glucose biosensor were 10.628 mV/mM and 0.998, respectively. After 28 days, RuO 2 /GR/MB-GOx-Nafion glucose biosensor still had relative sensitivity of 82.2%.