A New Test Facility to Characterize React and Wind \hbox Conductor
A new test facility was developed at CEA/Saclay in collaboration with the SigmaPhi Company in order to perform studies of a dry MgB 2 magnet operating at 10 K and medium range field (1 T up to 4 T). For a rapid use of the MgB 2 conductors in an industrial product, notably in the medical sector, the...
Gespeichert in:
Veröffentlicht in: | IEEE transactions on applied superconductivity 2014-06, Vol.24 (3), p.1-5 |
---|---|
Hauptverfasser: | , , , , , , , |
Format: | Artikel |
Sprache: | eng |
Schlagworte: | |
Online-Zugang: | Volltext bestellen |
Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
Zusammenfassung: | A new test facility was developed at CEA/Saclay in collaboration with the SigmaPhi Company in order to perform studies of a dry MgB 2 magnet operating at 10 K and medium range field (1 T up to 4 T). For a rapid use of the MgB 2 conductors in an industrial product, notably in the medical sector, the "react and wind" technique must be used to wind magnets. However, the reacted MgB 2 conductors have a minimum winding radius, classically around 100 mm, which is incompatible with the existing Saclay test facility. A new test facility has been constructed with a 600 A dc current power, a 300 mm diameter sample holder, and conduction cooling by a two-stage GM cryocooler. The background field for this test facility is provided by a NbTi coil, which has a warm bore of 350 mm and a maximum field of 3 T. This paper presents the design of this test facility, especially the design of the current leads, the insulated thermal contacts with the development of a new type of insulation based on aluminum nitride and the dry sample holder. Results of critical current tests in self-field are presented and compared with manufacturer data for a reacted MgB 2 conductor, a Ni/MgB 2 tape soldered on an OFHC copper stabilizer tape, supplied by Columbus Superconductors SpA. |
---|---|
ISSN: | 1051-8223 1558-2515 |
DOI: | 10.1109/TASC.2013.2282833 |