Effect of build orientation on the manufacturing process and the properties of stereolithographic dental ceramics for crown frameworks

Stereolithography (SLA) ceramic crown frameworks are suitable for clinical use, but the impact of SLA build orientation has not been identified. The purpose of this in vitro study was to investigate the effect of 3 build orientations on the physical and mechanical properties and the microstructure of SLA alumina dental ceramics. The physical and mechanical properties and microstructures of 3 different oriented SLA alumina ceramics (ZX, ZY, and XY) were evaluated by visual observation, hydrostatic weighing (n=10/group), Weibull analyses (n=30/group), scanning electron microscopy, 3-point flexural strength (n=30/group), fracture toughness (indentation, single-edge-V-notched-beam) (n=4/group), and Vickers hardness (n=15/group) testing. The hydrostatic weighing, 3-point flexural strength, fracture toughness, and Vickers hardness testing data were statistically analyzed (α=.05). The minimum resting period of slurries between the polymerization of 2 layers was shorter for the ZY- and ZX-oriented specimens and increased with the layer surface. The density and Vickers hardness of the SLA-manufactured specimens were similar for all groups (P>.05). The 95% confidence intervals of the Weibull moduli of the ZX- and ZY-oriented specimens were higher than that of the XY-oriented specimens, with no overlap fraction. The ZY-oriented specimens displayed significantly higher 3-point flexural strength (P