Influence of cycling temperature on the electrochromic properties of WO3//NiO devices built with various thicknesses

Electrochromic smart windows, which are able to vary their optical transmittance by the application of a voltage, improve the indoor comfort in buildings by controlling light and temperature. Among electrochromic devices, ECDs, WO3 and NiO are often associated leading to neutral color. This work focuses on the influence of the thickness of WO3 and NiO single layers on the ECD electrochemical and optical properties. Initial characterizations in lithium-based liquid electrolyte, show a non-linear evolution of the electrochemical capacity for each oxides vs. thickness while for similar thickness, WO3 thin films exhibit larger EC properties than NiO ones. The combinations of various WO3 and NiO thicknesses lead to ECDs of which capacity appears limited by the one of NiO, while the switch to a neutral color always remain. Besides, the influence of each oxide on the ECD cyclic voltammogram shape is discussed. Finally, the study of the cycling temperature, in the range −40°C to 80°C on the electrochromic properties of ITO/650nm-WO3/LiClO4-PC +PMMA/360nm-NiO/ITO shows an increase in performance with temperature nevertheless associated with signs of degradation above 60°C. At low temperature, the decrease in capacity is interestingly associated with a remaining significant optical contrast and the capacity recovery if the ECD is further cycled at RT. •Influence of WO3 and NiO thicknesses on ECD properties.•ECD capacity limited by NiO thin films.•Influence of the temperature on ECD properties.•Degradation of the ECD from 60°C.•Optically active ECD at low temperature.