Electrochemical promotion of the water–gas shift reaction on Pt/YSZ

[Display omitted] ► Electrochemical promotion of catalysis was applied on the water–gas shift reaction. ► A fuel cell type reactor (Pt/YSZ/Pt) was used. ► Negative polarization caused a pronounced increase in the catalytic rate. ► Positive polarization was found to poison the catalytic activity. The...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:Journal of catalysis 2011, Vol.283 (2), p.124-132
Hauptverfasser: Souentie, S., Lizarraga, L., Kambolis, A., Alves-Fortunato, M., Valverde, J.L., Vernoux, P.
Format: Artikel
Sprache:eng
Schlagworte:
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:[Display omitted] ► Electrochemical promotion of catalysis was applied on the water–gas shift reaction. ► A fuel cell type reactor (Pt/YSZ/Pt) was used. ► Negative polarization caused a pronounced increase in the catalytic rate. ► Positive polarization was found to poison the catalytic activity. The effect of electrochemical promotion of catalysis was investigated for the water–gas shift reaction over porous Pt catalyst electrodes interfaced with 8%mol Yttria-stabilized Zirconia. A fuel cell type electrochemical reactor was used at temperatures from 300 °C to 400 °C, under P H 2 O / P CO ratio values from 2.85 to 31. A negative order dependence of the catalytic reaction rate on P CO and a positive one on P H 2 O was found under open-circuit and polarization conditions. Positive potential application (+2.5 V), i.e., O 2− supply to the catalyst surface, causes a small decrease in the catalytic reaction rate, while negative potential application (−1.5 V) results in a pronounced rate increase, up to 200%, with apparent faradaic efficiency values up to 110. The rate increase obtained with negative polarization can be attributed to the weakening of the Pt–CO bond strength but also, to the increase in surface concentration of oxygen ion vacancies near the Pt-gas-support three-phase boundaries necessary for water dissociation.