Kaolinite-potassium acetate and halloysite-potassium acetate complexes prepared by mechanochemical, solution and homogenization techniques; a comparative study

Kaolinite- and halloysite-potassium acetate complexes were synthesized by co-grinding with solid potassium acetate (mechanochemical intercalation). The efficiency of mechanochemical intercalation was compared to the intercalation in solution and by homogenization. The effects of ageing and grinding parameters (grinding time, sample:grinding body mass ratio (SGMR), rotational speed) and the humidity on the intercalation were studied. The degree of intercalation increased exponentially with ageing of the samples prepared by mechanochemical and homogenization techniques. For the mechanochemical and homogenization techniques the required amount of potassium acetate per gram of kaolin (?0.4 g/g) was two orders of magnitude lower than that for the solution intercalation (78.6 g/g). The highest degree of intercalation (86%) and the lowest structural deformation were achieved by the mechanochemical method (1/4 h of co-grinding with 1:2 SGMR at 300 rpm), followed by 16 h ageing at 57% relative humidity.