Characterization of Thermo-Fixed Polymer Matrix Composite Reinforced with Cuban Zeolite Particles/Caracterizacion de material compuesto de matriz polimerica termofija reforzado con particulas de zeolita cubana

The present work is about the characterization of composite materials with thermoset polymeric matrix, orthophthalic polyester type and reinforcement with Cuban zeolite particles from San Andres, Holguin. Authors used different methods like sifted, scanning electron microscope (SEM) and X-rays diffraction, thermal analysis and cation exchange volumetric methods to analyze zeolite particles. The composite material was analyzed, with the use of test-tube, by mechanical test (hardness, traction, impact). Keywords: sifter, scanning electron microscope (SEM), X-rays diffraction, thermal analyzer, cation-exchange capacity RESUMEN. El presente trabajo, trata sobre la caracterización varios materiales compuestos con matriz polimérica termofija, del tipo poliéster ortoftálico y refuerzo con partículas de zeolita en proporciones de 3, 5, 7 y 10 porciento. La zeolita es de origen cubano, procedente de San Andrés en Holguín. Las partículas de zeolita fueron caracterizadas con métodos de tamizado, microscopía electrónica de barrido (MEB), difracción de rayos X, analizador térmico y volumétrico. Al material compuesto se le realizaron ensayos de dureza, tracción e impacto, obteniéndose así los valores límites para cada tipo de material. El aumento del porciento de zeolita aumentó la resistencia a la tracción y disminuyó la resistencia al impacto. La dureza se mantuvo similar para cada material. La microcopia electrónica de barrido mostró características que propician la adherencia entre el polímero y la zeolita. Palabras clave: tamizado, microscopía electrónica de barrido, analizador térmico, capacidad e intercambio catiónico.