Mechanical and thermal properties of cotton-bamboo fabric/glass fiber epoxy composites/Wlasciwosci mechaniczne i termiczne kompozytow epoksydowych wzmocnionych tkanina bawelniano-bambusowa i wloknem szklanym

Five-layer epoxy composites consisting of two outer layers made of glass fiber and three inner layers of cotton-bamboo fabric were obtained by compression molding. The influence of glass fiber content (35, 40, 45 and 50 wt%) and the order of stacking laminate layers on the mechanical properties (tensile, flexural, compressive, impact strength), thermal properties (TGA) and structure (FTIR, SEM) of the composites was investigated. The best mechanical and thermal properties were obtained with the content of 45 wt% glass fiber. Keywords: cotton-bamboo fabric, glass fiber, epoxy resin, composites. Metoda prasowania tlocznego otrzymano pieciowarstwowe kompozyty epoksydowe skladajace sic z dwoch warstw zewnetrznych wykonanych z wlokna szklanego oraz trzech wewnetrznych z tkaniny bawelniano-bambusowej. Zbadano wplyw zawartosci wlokna szklanego (35, 40, 45 i 50% mas) oraz kolejnosci ukladania warstw laminatu na wlasciwosci mechaniczne (wytrzymalosc na rozciaganie, zginanie i sciskanie oraz udarnosc), termiczne (TGA) oraz strukture (FTIR, SEM) kompozytow. Najlepsze wlasciwosci mechaniczne i termiczne uzyskano przy zawartosci 45% mas. wlokna szklanego. Slowa kluczowe: tkanina bawelniano-bambusowa, wlokno szklane, zywica epoksydowa, kompozyty.