Influence of Fibre Length on Properties of Glass-Fibre Reinforced Bark Particleboards /Utjecaj duljine vlakana na svojstva iverice od kore ojacane staklenim vlaknima

This study was carried out to assess the feasibility of glass fibres of various lengths (12 mm, 18 mm, 24 mm and 30 mm) as reinforcement on the mechanical performance of bark particleboards intended for thermal insulation. To evaluate their efficiency, the results of fibre reinforced particleboards at mass of 3wt% concentration were compared with plain bark based boards. Thermal, physical and mechanical properties (modulus of rupture, modulus of elasticity and internal bond) were determined on unreinforced and reinforced specimens. In general, the results of the thermal conductivity measurements indicated that the bark panels could potentially be used as feedstock for thermal insulation panels. However, the glass fibres lengths had a direct adverse effect on the mechanical behaviour of the bark particleboard, instead of providing synergistic reinforcement. Furthermore, the static bending properties, mainly the modulus of rupture, gradually decreased with increasing lengths of glass fibre. Keywords: utilization of bark; bio-based insulation panel; poplar bark Istrazivanje je provedeno kako bi se procijenila mogucnost uporabe staklenih vlakana razlicitih duljina (12; 18; 24 i 30 mm) kao materijala za ojacanje iverica proizvedenih od kore i namijenjenih toplinskoj izolaciji te kako bi se istrazio utjecaj tih vlakana na mehanicka svojstva iverica. Da bi se procijenio utjecaj staklenih vlakana, usporedena su svojstva iverica ojacanih staklenim vlaknima masenog udjela vlakana od 3% i iverica napravljenih od kore, bez ojacanja staklenim vlaknima. Usporedena su toplinska, fizicka i mehanicka svojstva (modul loma, modul elasticnosti i meduslojna cvrstoca) uzoraka ploca iverica s ojacanjem staklenim vlaknima i bez ojacanja. U osnovi, rezultati mjerenja toplinske vodljivosti pokazali su da bi se ploce od kore mogle potencijalno upotrebljavati za toplinsku izolaciju. Medutim, duljina staklenih vlakana imala je izravan nepovoljan utjecaj na mehanicka svojstva iverica od kore. Nadalje, svojstva statickog savijanja, uglavnom modul loma, postupno su se smanjivala s povecanjem duljine staklenih vlakana. Kljucne rijeci: uporaba kore; izolacijske ploce na prirodnoj bazi; kora od topolovine