Model for microhardness profile prediction of annealed AISI 1045 steel cylindrical bars subjected to torsion/ Modelo para la prediccion del perfil de microdureza de barras cilindricas de acero AIS11045 recocidas sometidas a torsion

In this work, the effect of the torsion process angle of twist and distance from the center of cylindrical bars on the microhardness profile of annealed AISI 1045 steel was studied. The results showed that the microhardness increase with the evaluated parameters and the hardening is related to the plastic deformation caused by the process rather than by microstructural transformations. Based on the experimental results, ANOVA-Pareto analysis was conducted proving that the angle of twist is the most influential control factor (59.35%) among the parameters investigated. Finally, a model to predict the microhardness profile from the torsion process is presented. KEYWORDS: AISI 1045, ANOVA, microhardness, torsion En este trabajo se estudio el efecto del angulo de giro del proceso de torsion y la distancia desde el centro en barras cilindricas en el perfil de microdureza del acero AISI 1045 recocido. Los resultados mostraron que la microdureza aumenta con los parametros evaluados y el endurecimiento se relaciona con la deformacion plastica causada por el proceso mas que por transformaciones microestructurales. Con base en los resultados experimentales, se realizo un analisis ANOVA-Pareto que demostro que el angulo de giro es el factor de control mas influyente (59,35%) entre los parametros investigados. Finalmente, se presenta un modelo para predecir el perfil de microdureza del proceso de torsion. AISI 1045, ANOVA, microdureza, torsion