Effect of Filler Type on the Properties of Rigid Polyurethane Foams at a Cryogenic Temperature

The effect of filler type and mass percentage on the properties of low-density rigid polyurethane foams at a temperature of 77K was investigated. The mechanical properties of foams of density 55-90 kg/m 3 filled with milled carbon fibers of average length of 100 and 60 μm and hollow glass microspheres of average diameter of 65 μm were compared. A considerable increase in the compressive elastic modulus in the foam rise direction with increasing filler content was observed. The compression strength of the foams in the parallel and perpendicular directions at the cryogenic temperature decreased upon introducing the milled carbon fibers of either type. The compression strength of the foams of density 90 kg/m 3 somewhat increased only upon introducing the glass microspheres.