Epoxy composites for aviation industry/Kompozyty epoksydowe do zastosowan w przemysle lotniczym

The effect of the amount (1.0 - 3.0 wt %) of bentonites modified with quaternary ammonium or phosphonium salts on the properties of epoxy resin/glass fibre composites was studied. It was found that the mechanical properties and flame resistance of the laminates filled with the modified bentonites were significantly better than of laminates produced from an unfilled resin. Scanning electron microscopy (SEM) and atomic force microscope (AFM) studies were also performed to investigate the adhesion between the laminate components. Keywords: epoxy resin, layered aluminosilicates, glass fibre, modification, composites, mechanical properties, flame retardation. Badano wplyw zawartosci (1,0-3,0 % mas.) bentonitow modyfikowanych solami amoniowymi i fosfoniowymi na wlasciwosci uzytkowe kompozytow na osnowie zywicy epoksydowej wzmocnionych wloknem szklanym. Oznaczono wlasciwosci mechaniczne oraz odpornosc na plomien otrzymanych laminatow. Wykonano rowniez badania za pomoca skaningowej mikroskopii elektronowej (SEM) i mikroskopii sil atomowych (AFM). Stwierdzono, ze laminaty z osnowa epoksydowa napelniona modyfikowanymi bentonitami charakteryzuja sie znacznie wieksza odpornoscia na plomien i lepszymi wlasciwosciami wytrzymalosciowymi niz laminaty wytworzone z zywicy nienapelnionej. Slowa kluczowe: zywica epoksydowa, glinokrzemiany warstwowe, wlokno szklane, modyfikacja, kompozyty, wlasciwosci mechaniczne, uniepalnianie.