Layered double hydroxides as transesterification catalysts and nanofillers for polyester resin/Warstwowe podwojne wodorotlenki jako katalizatory transestryfikacji i nanonapelniacze zywicy poliestrowej

Saturated polyester resins were prepared by reaction of dimethyl terephthalate with alkylene glycols in the presence of layered double hydroxides (hydrotalcites, HT). The effect of HT composition (cation and anion types) on the rate and progress of transesterification was investigated. It was found...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:Polimery 2015-03, p.160
Hauptverfasser: Kedzierski, Michal, Boncza-Tomaszewski, Zbigniew, Jaworska, Grazyna, Niska, Anna
Format: Artikel
Sprache:eng
Schlagworte:
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:Saturated polyester resins were prepared by reaction of dimethyl terephthalate with alkylene glycols in the presence of layered double hydroxides (hydrotalcites, HT). The effect of HT composition (cation and anion types) on the rate and progress of transesterification was investigated. It was found that zinc-aluminum HT intercalated with anionic form of aminolauric acid [HT(ZnAl)ALA] efficiently catalyzes transesterification process, increasing the rate of reaction or lowering its temperature when compared to the reaction with use of conventional organic tin catalyst. The polyester resin obtained in this way is transparent, which along with X-ray diffraction data indicates the delamination of clay layers and formation of nanocomposite. The limitation of using ALA-intercalated HT as an additive for polyesters used in coatings is coloration of the resin with an increase of the reaction temperature above 180°C. Colorless polyester was obtained using more thermally stable hydrotalcite intercalated with ethylenediaminetetraacetic acid, however, at the expense of significantly longer reaction time. Using HT(ZnAl)ALA catalyst a two-step synthesis of carboxyl polyester resin was performed and the obtained product was used as a component of powder coating formulation. Keywords: layered double hydroxides, hydrotalcite, intercalation, aminolauric acid, EDTA, transesterification, catalyst, polyester resins, nanocomposites. Streszczenie: Przeprowadzono synteze nasyconych zywic poliestrowych w reakcji tereftalanu dimetylowego z glikolami alkilenowymi, w obecnosci warstwowego podwojnego wodorotlenku typu hydrotalkitu (HT). Analizowano wplyw skladu HT na szybkosc i wydajnosc transestryfikacji. Najlepsze wyniki (zwiekszenie szybkosci reakcji lub obnizenie sredniej temperatury procesu w porownaniu z szybkoscia i temperatura reakcji prowadzonej w obecnosci tradycyjnego katalizatora organocynowego) uzyskano z zastosowaniem hydrotalkitu interkalowanego kwasem aminolaurynowym (ALA). Otrzymane w taki sposob zywice byly transparentne, co w polaczeniu z zanikiem refleksow hydrotalkitu w widmie XRD produktu transestryfikacji moze swiadczyc o utworzeniu sie delaminowanego nanokompozytu. Wykorzystanie HT interkalowanego ALA w zywicach poliestrowych stosowanych do powlok jest ograniczone ze wzgledu na zabarwienie pojawiajace sie w temperaturze powyzej 180°C. W reakcji prowadzonej z udzialem bardziej stabilnego termicznie hydrotalkitu modyfikowanego kwasem etylenodiaminotetraoctowym ot
ISSN:0032-2725
DOI:10.14314/polimery.2015.160