Zinc-doped hydroxyapatite and poly

Hydroxyapatite (HA) is a bioceramic material that shares similar crystal and chemical structures with inorganic components of the bone. However, HA lacks osteoinductive activity and has a brittle nature, making it challenging to apply for direct load-bearing bone applications. In this study, we used a wet chemical method to synthesize zinc-doped hydroxyapatite powders with different Zn/(Zn+Ca) molar ratios of 0, 0.025, 0.05, and 0.1. The corresponding Zn-HA was designated as HA, Zn2.5-HA, Zn5-HA, and Zn10-HA. The Zn-HA powders at 30 wt% were used to fabricate poly(propylene fumarate) (PPF)-based nanocomposite scaffolds (HA/PPF, Zn2.5-HA/PPF, Zn5-HA/PPF, and Zn10-HA/PPF). The physical properties of obtained scaffolds were examined by scanning electron microscopy, energy-dispersive X-ray spectroscopy (EDS), transmission electron microscopy (TEM), and atomic force microscopy (AFM). Live/dead cell viability assay showed that these scaffolds were biocompatible and supported excellent adhesion of MC3T3-E1 preosteoblast cells. Additionally, the proliferation of cells was detected at 1, 4, and 7 days on these scaffolds. Alkaline phosphatase (ALP) activity measurement and alizarin red staining showed good osteogenic differentiation and matrix mineralization for MC3T3-E1 cells growing on these scaffolds. Taken together, the results here indicate that Zn5-HA/PPF nanocomposite scaffolds are promising scaffold material for bone tissue engineering.