SYNTHESIS OF M41S MATERIALS

M41S materials are synthesized from an aqueous reaction mixture comprising sources of an oxide of a tetravalent element Y, hydroxyl ions and an organic surfactant R', wherein R' comprises an ion of the formula R1R2R3R4Q, wherein Q is nitrogen or phosphorus and wherein at least one of R1, R2, R3 and R4 is aryl or alkyl of from 6 to about 36 carbon atoms or combinations thereof, the remainder of R1, R2, R3 and R4 being selected from the group consisting of hydrogen, alkyl of from 1 to 5 carbon atoms and combinations thereof, and wherein the OH/surfactant molar ratio is in the approximate range 0.9-1.2, more preferably 1.0-1.15. By controlling the surfactant level within the above ranges it is found that high quality M41S materials with excellent adsorption properties can be produced at surfactant utilization levels. Cette invention concerne des matériaux du type M41S qui sont synthétisés à partir d'un mélange de réaction aqueux. Ce mélange comprend des sources d'un oxyde d'un élément tetravalent Y, ainsi que des ions hydroxyle et un tensioactif organique R'. R' comprend un ion correspondant à la formule R1R2R3R4Q où Q représente azote ou phosphore, tandis que l'un au moins des éléments R1, R2, R3 ou R4 représente un aryle ou un alkyle comportant de 6 à environ 36 atomes de carbone ou, encore, des combinaisons de ces derniers. Les éléments R1, R2, R3 et R4 restant sont quant à eux choisis dans le groupe comprenant hydrogène, un alkyle comportant de 1 à 5 atomes de carbone ou, encore, des combinaisons de ces derniers. Le rapport molaire OH/tensioactif varie approximativement entre 0,9 et 1,2, de préférence entre 1,0 et 1,15. En maintenant la teneur en tensioactif dans les limites susmentionnées, il possible de produire, à des niveaux d'utilisation de tensioactifs, des matériaux de type M41S d'une grande qualité et qui possèdent d'excellentes capacités d'adsorption.