METHOD OF OBTAINING ALUMINOSILICON ALLOY CONTAINING 2-22 PER CENT BY WEIGHT OF SILICON

The method consists in charging in the form of a cone, crystalline silicon on the hearth of a reverberatory furnace, pouring the liquid aluminium into the bath of the furnace at a temperature of 780-820C while continually mixing the aluminosilicon melt by means of a jet formed of the same melt, which is directed to the base of the cone of the charged silicon at a speed of the jet, along its axis, of 0.5-0.8 m/sec; simultaneously with the start of the mixing the temperature of the melt in the bath of the furnace is cooled down to 670-750C and mixing is continued at this temperature. The alloy may be used in the automobile and tractor industry, as well as for production of consumer goods. Le procédé consiste à charger du silicium cristallin, sous forme d'un cône, sur le foyer d'un four à réverbères, à verser l'aluminium liquide dans le bain du four à une température de 780-800°C en brassant la coulée d'alumino-silicium au moyen d'un jet formé par ladite coulée, le jet étant dirigé vers la base du cône de silicium chargé à une vitesse axiale du jet de 0,5 à 0,8 m/sec; en même temps que le démarrage du brassage, la température de la coulée du bain du four est abaissée à 670-750°C et on continue le brassage à cette température. L'alliage peut être utilisé dans l'industrie des automobiles et des tracteurs, ainsi que pour la production de biens de consommation.