PSEUDOBOEHMITE, METHOD FOR PRODUCING PSEUDOBOEHMITE, METHOD FOR PRODUCING CARRIER, AND METHOD FOR PRODUCING HYDROGENATION REFINING CATALYST

Provided is a pseudoboehmite used as a raw material of a highly active hydrogenation refining catalyst. The crystallite diameter D020 of the pseudoboehmite in a direction perpendicular to the (020) plane of the pseudoboehmite is 2.0-3.5 nm. The crystallite diameter D120 of the pseudoboehmite in a direction perpendicular to the (120) plane of the pseudoboehmite is 2.5-4.5 nm. D020/D120 is 0.8-1.3. The volume of pores having a pore diameter of 20-600 Å among the pores in the pseudoboehmite is 0.80-1.20 ml/g. The volume of the pores is measured by the nitrogen adsorption method. The pH that indicates the isoelectric point of the pseudoboehmite in water is 8.8 or more. L'invention concerne de la pseudobœhmite utilisée en tant que matière première d'un catalyseur de raffinage par hydrogénation hautement actif. Le diamètre des cristallites D020 de la pseudobœhmite dans une direction perpendiculaire au plan (020) de la pseudobœhmite est compris entre 2,0 et 3,5 nm. Le diamètre des cristallites D120 de la pseudobœhmite dans une direction perpendiculaire au plan (120) de la pseudobœhmite est compris entre 2,5 et 4,5 nm. D020/D120 est compris entre 0,8 et 1,3. Le volume des pores ayant un diamètre de 20 à 600 Å parmi les pores de la pseudobœhmite est compris entre 0,80 et 1,20 ml/g. Le volume des pores est mesuré par le procédé d'adsorption d'azote. Le pH qui indique le point isoélectrique de la pseudobœhmite dans l'eau est de 8,8 ou plus. 活性に優れた水素化精製触媒の原料に用いられる擬ベーマイトが提供される。擬ベーマイトの（０２０）面に垂直な方向における擬ベーマイトの結晶子径Ｄ０２０は、２．０ｎｍ以上３．５ｎｍ以下である。擬ベーマイトの（１２０）面に垂直な方向における擬ベーマイトの結晶子径Ｄ１２０は、２．５ｎｍ以上４．５ｎｍ以下である。Ｄ０２０／Ｄ１２０は、０．８以上１．３以下である。擬ベーマイト中の細孔のうち細孔径が２０Å以上６００Å以下である細孔の容積は、０．８０ｍｌ／ｇ以上１．２０ｍｌ／ｇ以下である。細孔の容積は、窒素吸着法によって測定される。水中における擬ベーマイトの等電点を示すｐＨは、８．８以上である。