STEEL SHEET AND HIGH STRENGTH PRESS HARDENED STEEL PART HAVING EXCELLENT BENDING ANISOTROPY AND METHOD OF MANUFACTURING THE SAME

Steel sheet and high strength press hardened steel part and method of manufacturing the same Steel sheet having a chemical composition comprising in wt% C : 0.2 - 0.4%, Mn : 0.8 - 2.0%, Si : 0.1 - 0.5 %, Al : 0.01 - 0.1 %, Ti: 0.01 - 0.1 %, B: 0.0005 - 0.005 %, P ≤ 0.040 %, Ca ≤ 0.01%, S ≤ 0.006 %, N ≤ 0.01 %, Said steel sheet comprising from the bulk to the surface of the coated steel sheet a bulk and a skin layer occupying the outermost 10% of the thickness on either side of the bulk, said bulk comprising an inclusion population wherein the sum of clustering indexes of MnS and TiN / Ti(C,N) inclusions is less than or equal to 300µm/mm². This allows to manufacture hot pressed parts having a tensile strength equal to or greater than 1300MPa and a bending anisotropy equal to or lower than 7°. Tôle d'acier et pièce d'acier trempé à la presse à haute résistance et procédé de fabrication de celles-ci, la tôle d'acier ayant une composition chimique comprenant, en % en poids, C : de 0,2 à 0,4 %, Mn : de 0,8 à 2,0 %, Si : de 0,1 à 0,5 %, Al : de 0,01 à 0,1 %, Ti : de 0,01 à 0,1 %, B : de 0,0005 à 0,005 %, P ≤ 0,040 %, Ca ≤ 0,01 %, S ≤ 0,006 %, N ≤ 0,01%, ladite tôle d'acier comprenant entre la masse et la surface de la tôle d'acier revêtue une masse et une couche de surface occupant les 10 % les plus à l'extérieur de l'épaisseur de chaque côté de la masse, ladite masse comprenant une population d'inclusion, la somme des indices de regroupement des inclusions de MnS et TiN/Ti(C,N) étant inférieure ou égale à 300 µm/mm2. Ceci permet de fabriquer des pièces pressées à chaud ayant une résistance à la traction supérieure ou égale à 1 300 MPa et une anisotropie de flexion inférieure ou égale à 7°.