DECORATIVE FILM

One embodiment of the present invention relates to a decorative film. The decorative film includes a substrate layer and an adhesive layer. The stress-relaxation rate of the substrate layer as measured by a stress-relaxation test is 40% to 100% inclusive, the stress after 30 sec is 2.0 N or less, the ratio of the loss tangent at 80°C and the loss tangent at 23°C (80°C loss tangent/23°C loss tangent) of the adhesive layer as measured by a dynamic viscoelasticity test is 0.45 to 0.80, and the peeling distance of the adhesive layer as measured by a constant-load peeling test is less than 100 mm. Un mode de réalisation de la présente invention concerne un film décoratif. Le film décoratif comprend une couche de substrat et une couche adhésive. Le taux de relaxation de contrainte de la couche de substrat tel que mesuré par un test de relaxation de contrainte est de 40% à 100% inclus, la contrainte après 30 sec est de 2,0 N ou moins, le rapport de la tangente de perte à 80°C et de la tangente de perte à 23°C (tangente de perte de 80°C/tangente de perte de 23°C) de la couche adhésive telle que mesurée par un test de viscoélasticité dynamique est de 0,45 à 0,80, et la distance de pelage de la couche adhésive telle que mesurée par un test de pelage à charge constante est inférieure à 100 mm. 本発明の一実施形態は、加飾フィルムに関し、該加飾フィルムは、基材層と粘着剤層を含み、前記基材層の、応力緩和性試験で測定される応力緩和率が４０％以上１００％以下であり、３０秒後の応力が２．０Ｎ以下であり、前記粘着剤層の、動的粘弾性試験で測定される８０℃の損失正接と２３℃の損失正接の比（８０℃損失正接／２３℃損失正接）が０．４５～０．８０であり、かつ、前記粘着剤層の、定荷重剥離性試験で測定される剥離距離が１００ｍｍ未満である。