COATING COMPOSITION

The present invention provides a coating composition that has excellent stability over time, and exhibits excellent transparency when formed into a coating film. The present invention is a coating composition that comprises a zirconium element-containing metal oxide (A) and a silane compound (B), the coating composition being characterized in that the zirconium element-containing metal oxide (A) has a zeta potential value of at least 30 mV as measured by the following method. 10 mass% of a zirconium element-containing metal oxide (A) aqueous dispersion is measured at room temperature (25 °C) by using an electrophoretic laser doppler method. La présente invention concerne une composition de revêtement présentant une excellente stabilité dans le temps, et présentant une excellente transparence lorsqu'elle est formée en film de revêtement. La présente invention concerne une composition de revêtement comprenant un oxyde métallique contenant un élément zirconium (A) et un composé silane (B), la composition de revêtement étant caractérisée en ce que l'oxyde métallique contenant un élément zirconium (A) a une valeur de potentiel zêta d'au moins 30 mV telle que mesurée par le procédé suivant. Procédé de mesure du potentiel zêta On mesure 10 % en masse d'une dispersion aqueuse d'oxyde métallique contenant un élément de zirconium (A) à la température ambiante (25 °C) en utilisant un procédé électrophorétique à laser doppler. 本発明は、経時安定性に優れ、かつ、塗膜を形成した際に優れた透明性を発揮するコーティング用組成物を提供する。 本発明は、ジルコニウム元素含有金属酸化物（Ａ）とシラン化合物（Ｂ）とを含むコーティング用組成物であって、該ジルコニウム元素含有金属酸化物（Ａ）は、下記の方法により測定されるゼータ電位の値が３０ｍＶ以上であることを特徴とするコーティング用組成物である。 ＜ゼータ電位の測定方法＞ １０質量％のジルコニウム元素含有金属酸化物（Ａ）水分散液を電気泳動レーザードップラー法により室温（２５℃）で測定する。