GREY CAST IRON, IN PARTICULAR FOR DISC BRAKE COMPONENTS

The present invention relates to a grey cast iron comprising, within a ferrous matrix: an amount of carbon between 3.60 and 3.90% by weight; an amount of silicon between 1.40 and 1.90% by weight; an amount of titanium not higher than 0.10% by weight; an amount of boron between 0.04 and 0.07% by weight; an amount of vanadium between 0.07 and 0.14% by weight; an amount of manganese between 0.60% and 0.90% by weight; an amount of nickel not higher than 0.20% by weight; an amount of chromium not higher than 0.35% by weight; an amount of copper not higher than 0.35% by weight; an amount of phosphorus not higher than 0.10% by weight; an amount of sulphur not higher than 0.12% by weight; an amount of tin not higher than 0.10% by weight; an amount of molybdenum not higher than 0.10% by weight. La présente invention concerne une fonte grise comprenant, dans une matrice ferreuse : une quantité de carbone comprise entre 3,60 et 3,90 % en poids ; une quantité de silicium comprise entre 1,40 et 1,90 % en poids ; une quantité de titane qui n'est pas supérieure à 0,10 % en poids ; une quantité de bore comprise entre 0,04 et 0,07 % en poids ; une quantité de vanadium comprise entre 0,07 et 0,14 % en poids ; une quantité de manganèse comprise entre 0,60 % et 0,90 % en poids ; une quantité de nickel qui n'est pas supérieure à 0,20 % en poids ; une quantité de chrome qui n'est pas supérieure à 0,35 % en poids ; une quantité de cuivre qui n'est pas supérieure à 0,35 % en poids ; une quantité de phosphore qui n'est pas supérieure à 0,10 % en poids ; une quantité de soufre qui n'est pas supérieure à 0,12 % en poids ; une quantité d'étain qui n'est pas supérieure à 0,10 % en poids ; une quantité de molybdène qui n'est pas supérieure à 0,10 % en poids.