COLORED GLASS ARTICLES HAVING IMPROVED MECHANICAL DURABILITY

A colored glass article includes greater than or equal to 50 mol% and less than or equal to 70 mol% SiO2, greater than or equal to 10 mol% and less than or equal to 17.5 mol% Al2O3, greater than or equal to 3 mol% and less than or equal to 10 mol% B2O3, greater than or equal to 8.8 mol% and less than or equal to 14 mol% Li2O, greater than or equal to 1.5 mol% and less than or equal to 8 mol% Na2O, and greater than 0 mol% and less than or equal to 2 mol% Cr2O3. R2O + RO - Al2O3 is greater than or equal to 0.5 mol% and less than or equal to 6 mol%. Al2O3 + MgO + ZnO is greater than or equal to 12 mol% and less than or equal to 22 mol%. L'invention concerne un article en verre comprenant une quantité supérieure ou égale à 50 % en moles et inférieure ou égale à 70 % en moles de SiO2; une quantité supérieure ou égale à 10 % en moles et inférieure ou égale à 17,5 % en moles d'Al2O3; une quantité supérieure ou égale à 3 % en moles et inférieure ou égale à 10 % en moles de B2O3; une quantité supérieure à 8,8 % en moles et inférieure ou égale à 14 % en moles de Li2O; une quantité supérieure ou égale à 1,5 % en moles et inférieure ou égale à 8 % en moles de Na2O; et une quantité supérieure ou égale à 0 % en moles et inférieure ou égale à 2 % en moles de Cr2O3. R2O + RO - Al2O3 est supérieur ou égal à 0,5 % en moles et inférieur ou égal à 6 % en moles. Al2O3 + MgO + ZnO est supérieur ou égal à 12 % en moles et inférieur ou égal à 22 % en moles.