THERMALLY ANNEALED GRATINGS IN COATED FIBER AND RELATED SYSTEMS AND METHODS

Described herein are systems, methods, and articles of manufacture for a coated fiber modified by actinic radiation to increase back-scattering, which experiences very little back scattering decay at a temperature and time of exposure that is sufficient to noticeably degrade the coating and/or noticeably degrade the optical fiber due to outgassing of hydrogen from the coating, wherein an optical fiber comprises a fiber length, a coating having a treated coating weight, wherein the treated coating weight is at least 25% less of an original coating weight prior to an annealing treatment, and an optical back-scatter along the fiber length greater than a Rayleigh back-scattering over the fiber length, wherein the optical back-scatter does not decrease along the fiber length by more than 3 dB after exposure to annealing treatment. L'invention concerne des systèmes, des procédés, et des articles de fabrication pour une fibre revêtue modifiée par un rayonnement actinique pour augmenter la rétrodiffusion, qui subit une très faible décroissance de la rétrodiffusion à une température et un temps d'exposition qui est suffisant pour dégrader sensiblement le revêtement et/ou dégrader sensiblement la fibre optique due au dégazage de l'hydrogène du revêtement, une fibre optique comprenant une longueur de fibre, un revêtement ayant un poids de revêtement traité, le poids de revêtement traité étant d'au moins 25 % inférieur à un poids de revêtement d'origine avant un traitement de recuit, et une rétrodiffusion optique le long de la longueur de fibre supérieure à une rétrodiffusion de Rayleigh sur la longueur de la fibre, la rétrodiffusion optique ne diminuant pas le long de la longueur de fibre de plus de 3 dB après exposition à un traitement de recuit.