HIGH STRENGTH THERMALLY STABLE NICKEL-BASE ALLOYS

An alloy includes a composition, in weight percent, of aluminum from about 1.3% to about 1.8%, cobalt from about 1.5% to about 4.0%, chromium from about 18.0% to about 22.0%, iron from about 4.0% to about 10.0%, molybdenum from about 1.0% to about 3.0%, niobium from about 1.0% to about 2.5%, titanium from about 1.3% to about 1.8%, tungsten from about 0.8% to about 1.2%, carbon from about 0.01% to about 0.08%, and balance nickel and incidental impurities. The alloy has a stress rupture life at 700°C and 393.7 MPa (57.1 ksi) of at least 300 hours and a room temperature percent elongation of at least 15% after aging at 700°C for 1,000 hours. La présente invention concerne un alliage qui comprend une composition comprenant, en pourcentage en poids, d'environ 1,3 % à environ 1,8 % d'aluminium, d'environ 1,5 % à environ 4,0 % de cobalt, d'environ 18,0 % à environ 22,0 % de chrome, d'environ 4,0 % à environ 10,0 % de fer, d'environ 1,0 % à environ 3,0 % de molybdène, d'environ 1,0 % à environ 2,5 % de niobium, d'environ 1,3 % à environ 1,8 % de titane, d'environ 0,8 % à environ 1,2 % de tungstène, d'environ 0,01 % à environ 0,08 % de carbone, et le reste du nickel et d'impuretés accidentelles. L'alliage a une durée de vie à la rupture par contrainte à 700 °C et 393,7 MPa (57,1 ksi) d'au moins 300 heures et un pourcentage d'allongement à température ambiante d'au moins 15 % après vieillissement à 700 °C pendant 1000 heures.