GRAIN ORIENTED ELECTRICAL STEEL SHEET AND METHOD FOR MANUFACTURING SAME

A method for manufacturing a grain oriented electrical steel sheet according to an embodiment of the present invention comprises the steps of: hot-rolling a slab to prepare a hot-rolled sheet, the slab containing, in weight%, Si: 2.5-4.0%, C: 0.03-0.09%, Al: 0.015-0.040%, Mn: 0.04-0.15%, S: 0.01% or less (0% excluded), N: 0.002-0.012%, and the balance being Fe and other inevitably incorporated impurities; cold-rolling the hot-rolled sheet to prepare a cold-rolled sheet; performing primary recrystallization annealing on the cold-rolled sheet; and performing secondary recrystallization annealing on the cold-rolled sheet that has been primary recrystallization annealed. Un procédé de fabrication d'une tôle d'acier magnétique à grains orientés selon un mode de réalisation de la présente invention comprend les étapes consistant à : laminer à chaud une brame pour préparer une tôle laminée à chaud, la brame contenant, en % en poids, Si : 2,5 à 4,0 %, C : 0,03 à 0,09 %, Al : 0,015 à 0,040 %, Mn : 0,04 à 0,15 %, S : 0,01 % ou moins (à l'exclusion de 0 %), N : 0,002 à 0,012 %, le reste étant du Fe et d'autres impuretés inévitablement incorporées ; laminer à froid la tôle laminée à chaud pour préparer une tôle laminée à froid ; effectuer un recuit de recristallisation primaire sur la tôle laminée à froid ; et effectuer un recuit de recristallisation secondaire sur la tôle laminée à froid qui a été soumise au recuit de recristallisation primaire. 본 발명의 일 실시예에 의한 방향성 전기강판의 제조 방법은 중량%로, Si: 2.5 내지 4.0%, C: 0.03 내지 0.09%, Al: 0.015 내지 0.040%, Mn: 0.04 내지 0.15%, S : 0.01% 이하(0%를 제외함) 및 N: 0.002 내지 0.012% 포함하고, 잔부 Fe 및 기타 불가피하게 혼입되는 불순물을 포함하고, 잔부 Fe 및 기타 불가피하게 혼입되는 불순물을 포함하는 슬라브를 열간압연하여 열연판을 제조하는 단계; 열연판을 냉간압연하여 냉연판을 제조하는 단계; 냉연판을 1차 재결정 소둔하는 단계; 및 1차 재결정 소둔이 완료된 냉연판을 2차 재결정 소둔하는 단계를 포함한다.