THIN FIBER CEMENT ROOF TILES COMPRISING CORE-SHELL EMULSIONS HAVING IMPROVED IMPACT RESISTANCE

The present invention provides fiber cement articles, such as roof tiles having improved impact and hail resistance and methods for making them. The fiber cement articles comprise cement, an optional filler, reinforcing fibers, such as poly(vinyl alcohol) fibers or a mixture of cellulosic and synthetic fibers, one or more core-shell aqueous emulsion polymers having a crosslinked rubbery core with a calculated glass transition temperature (calculated Tg) of from -20 to -140 °C, and an at least partially grafted acrylic or vinyl shell polymer having a calculated Tg of from 20 to 170 °C, and having a Z-average primary particle size of from 55 to 800 nm, or, preferably, from 140 to 650 nm. The solids weight ratio of the crosslinked rubbery core to the shell of the core-shell aqueous emulsion polymer may range from 85:20 to 97:3. La présente invention concerne des articles en fibrociment, tels que des tuiles de toit présentant une résistance améliorée aux chocs et à la grêle et leurs procédés de fabrication. Les articles en fibrociment comprennent du ciment, une charge facultative, des fibres de renforcement, telles que des fibres de poly(alcool vinylique) ou un mélange de fibres cellulosiques et de fibres synthétiques, un ou plusieurs polymères en émulsion aqueuse cœur-écorce ayant un cœur caoutchouteux réticulé dont la température de transition vitreuse calculée (Tg calculée) est de -20 à -140 °C, et un polymère d'écorce acrylique ou vinylique au moins partiellement greffé ayant une Tg calculée de 20 à 170 °C, et dont la taille de particule primaire moyenne en Z est de 55 à 800 nm, ou, de préférence, de 140 à 650 nm. Le rapport pondéral des solides du cœur caoutchouteux réticulé à l'écorce du polymère en émulsion aqueuse cœur-écorce peut aller de 85:20 à 97:3.