STEEL SHEET FOR NON-ORIENTED ELECTROMAGNETIC STEEL SHEET

Provided is a steel sheet for a non-oriented electromagnetic steel sheet, which contains 0.0040% or less of C, 1.9-3.5% of Si, 0.10-3.0% of Al, 0.10-2.0% of Mn, 0.09% or less of P, 0.005% or less of S, 0.0040% or less of N and 0.0060% or less of B, with the remainder comprising Fe and impurities. The recrystallization ratio is less than 50% in a structure of a cross section in the sheet thickness direction at positions 10 mm towards the center of the sheet width from both edges in the sheet width direction. If W denotes the sheet width, the recrystallization ratio is 50% or more in a structure of a cross section in the sheet thickness direction at positions corresponding to 1/4W from both edges in the sheet width direction. La tôle d'acier pour une tôle d'acier électromagnétique à grains non orientés selon l'invention contient 0,0040 % ou moins de C, de 1,9 à 3,5 % de Si, de 0,10 à 3,0 % d'Al, de 0,10 à 2,0 % de Mn, 0,09 % ou moins de P, 0,005% ou moins de S, 0,0040% ou moins de N et 0,0060% ou moins de B, le reste étant du Fe et des impuretés inévitables. Le rapport de recristallisation est inférieur à 50 % dans une structure d'une section transversale dans la direction de l'épaisseur de la tôle à des endroits situés à 10 mm vers le centre de la largeur de la tôle à partir des deux bords dans la direction de la largeur de la tôle. Si W représente la largeur de la tôle, le rapport de recristallisation est de 50 % ou plus dans une structure d'une section transversale dans la direction de l'épaisseur de la tôle à des endroits correspondant à 1/4W à partir des deux bords dans la direction de la largeur de la tôle. Ｃ：０．００４０％以下、Ｓｉ：１．９％以上３．５％以下、Ａｌ：０．１０％以上３．０％以下、Ｍｎ：０．１０％以上２．０％以下、Ｐ：０．０９％以下、Ｓ：０．００５％以下、Ｎ：０．００４０％以下、Ｂ：０．００６０％以下を含有し、残部がＦｅおよび不純物からなり、板幅方向の両端部のそれぞれから板幅中央へ１０ｍｍの各位置における板厚方向断面の組織の再結晶率が５０％未満であり、板幅をＷとするとき、板幅方向の両端部からそれぞれ１／４Ｗの位置における板厚方向断面の組織の再結晶率が５０％以上である無方向性電磁鋼板用鋼板を提供する。