HOT-STAMPED COMPONENT, AND METHOD FOR MANUFACTURING SAME

An embodiment of the present invention discloses a method for manufacturing a hot-stamped component, the method comprising: a step for injecting a blank into a heating furnace provided with a plurality of compartments having different temperature ranges; a multi-stage heating step for heating the blank in stages; and a soaking step for heating the blank at a temperature of Ac3 to 1,000°C, wherein, in the multi-stage heating step, the temperature condition in the heating furnace satisfies the following expression. 0 < (Tg - Ti) / Lt < 0.025 ℃/mm (In the expression, Tg represents the soaking temperature (°C), Ti represents the temperature (°C) at the entrance of the heating furnace, and Lt represents the length (mm) of the multi-stage heating). Un mode de réalisation de la présente invention concerne un procédé de fabrication d'un composant estampé à chaud, le procédé comprenant : une étape d'injection d'une ébauche dans un four de chauffage doté d'une pluralité de compartiments présentant des plages de température différentes; une étape de chauffage à étages multiples destinée à chauffer l'ébauche par étages; et une étape de trempage destinée à chauffer l'ébauche à une température de Ac3 à 1 000 °C, dans l'étape de chauffage à étages multiples, la condition de température dans le four de chauffage satisfaisant l'expression suivante. 0 < (Tg - Ti) / Lt < 0,025 ℃/mm (Dans l'expression, Tg représente la température de trempage (°C), Ti représente la température (°C) à l'entrée du four de chauffage et Lt représente la longueur (mm) du chauffage à étages multiples). 본 발명의 일 실시예는, 서로 다른 온도 범위를 가지는 복수의 구간을 구비한 가열로 내로 블랭크를 투입하는 단계; 상기 블랭크를 단계적으로 가열하는 다단 가열 단계; 및 상기 블랭크를 Ac3 내지 1,000℃의 온도로 가열하는 균열 가열 단계;를 포함하고, 상기 다단 가열 단계에서 상기 가열로 내의 온도 조건은 하기 수학식을 만족하는 핫 스탬핑 부품의 제조 방법을 개시한다. 0 < (Tg - Ti) / Lt < 0.025℃/mm (상기 수학식에서 Tg는 균열 가열 온도(℃), Ti는 가열로 초입 온도(℃), Lt는 다단 가열 길이(mm)).